Method for molecular bonding of silicon and glass substrates

ABSTRACT

A method for bonding a first substrate having a first surface to a second substrate having a second surface. This method includes the steps of holding the first substrate by at least two support points, positioning the first substrate and the second substrate so that the first surface and the second surface face each other, deforming the first substrate by applying between at least one pressure point and the two support points a strain toward the second substrate, bringing the deformed first surface and the second surface into contact, and progressively releasing the strain to facilitate bonding of the substrates while minimizing or avoiding the trapping of air bubbles between the substrates.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 13/248,763, filed Sep. 29, 2011, the entire content of which is expressly incorporated herein by reference thereto.

FIELD OF THE INVENTION

The field of this invention is that of Silicon-On-Glass (SiOG) structures. More precisely, the invention relates to an improved method for making such structures.

BACKGROUND OF THE INVENTION

Silicon-On-Insulator (SOI) technology is becoming increasingly important for high performance thin film transistors, solar cells, etc. SOI wafers consist of a thin useful layer of substantially single crystal silicon having a thickness that generally is less than one micron, with the layer supported on an insulating material.

Various structures and various ways of obtaining such wafers are known. Typically, structures used are formed with a thin film of silicon bonded to another silicon wafer with an oxide insulator layer in between.

Because of its rather high thickness, in particular as compared to the other parts, a major fraction of the cost of such structures has been the cost of the silicon substrate which supports the oxide layer, topped by the thin silicon layer. Thus, to lower the cost of SOI structures, the use of a support substrate made of materials less expensive than silicon has been tried, in particular glass or glass-ceramics.

SOI structures using such glass-based substrates are called SiOG structures, as already mentioned. Processes for providing an SiOG structure are, for example, described by U.S. Pat. No. 7,176,528. Such a process is represented by FIG. 1. A source substrate 1 b, generally made of silicon, is implanted with ionic species such as hydrogen. The implantation leads to the creation of a buried, weakened zone 7. Further, the source substrate 1 b is bonded with a glass-based support substrate 1 a and then separated by splitting the source substrate 1 b to a depth corresponding to the penetration depth of the implanted species. In this way, an SiOG structure containing the original glass-based support substrate 1 a and a layer 8 from the source substrate 1 b, and a remaining delaminated substrate being a part of the former source substrate 1 b are produced.

It is not a simple matter, however, to replace a traditional SOI support substrate with a glass-based support substrate. One potential issue with SiOG is that a glass-based support substrate 1 a generally contains metals (in particular, alkali metals) and other components, which may be harmful to silicon or other semiconductor materials of the useful layer 8 from the source substrate 1 b. Therefore, a barrier layer is generally required between the glass-based support substrate 1 a and the source substrate 1 b. Moreover, this barrier layer may facilitate the bonding between the silicon layer 8 and the glass-based support substrate 1 a by making hydrophilic the bonding surface of the silicon layer 8. In this regard, a SiO₂ layer can be used as a barrier layer to obtain hydrophilic surface conditions between the glass-based support substrate 1 a and the silicon layer 8.

A native SiO₂ layer can be directly formed on a silicon source substrate 1 b by exposing it to the atmosphere prior to bonding. Alternatively, when anodic bonding is used, the anodic bonding process produces “in situ” a SiO₂ layer between the silicon source substrate 1 b and the glass-based support substrate 1 a. Also, a SiO₂ layer can be actively deposited or grown on the source substrate 1 b prior to bonding.

U.S. Pat. No. 7,176,528 discloses another type of a barrier layer, which can be provided by the anodic bonding process. This barrier layer is a modified top layer of glass in the glass-based support substrate 1 a, namely, a glass layer having a reduced level of ions. The disclosed anodic bonding substantially removes alkali and alkali earth glass constituents and other positive modifier ions that are harmful for silicon for a distance of about 100 nm to form a thick top layer on the glass-based support substrate 1 a.

Molecular bonding is then usually performed by putting the two substrate surfaces into very close contact. Pressure is applied to the substrates by means of a mechanical piston in order to locally approach the two surfaces at a sub-nanometer scale distance. In case of hydrophilic bonding, it leads to the establishment of hydrogen bonds in between water molecules adsorbed at the two hydrophilic surfaces. With the progressive establishment of hydrogen bonds at the edges of the already bonded area, the bonded area gradually increases. A bonding wave thus propagates until it reaches the edge of at least one of the substrates. Any disturbance of the bonding wave propagation or of the bonding wave closure at the edge of a substrate may lead to the trapping of an air bubble 9. Such air bubbles 9 locally prevent the substrates to bond, which causes holes in the layer 8 separated from the source substrate 1 b and bonded to the glass-based support substrate 1 a, as represented in FIG. 2.

There is consequently a need for a method for bonding the two substrates that avoids the trapping of bubbles during the molecular bonding.

SUMMARY OF THE INVENTION

The present invention now provides high quality bubble-free bonded substrates of silicon and glass. Moreover, the present invention also aims at providing an efficient bonding of a series of substrates, in order to speed up industrial processes and save cost.

For these purposes, the present invention provides a method for bonding a first substrate having a first surface to a second substrate having a second surface, characterized in that it comprises:

-   -   holding the first substrate by at least two support points;     -   positioning the first substrate and the second substrate so that         the first surface and the second surface face each other;     -   deforming the first substrate by applying between at least one         pressure point and the two support points, a strain toward the         second substrate;     -   bringing the deformed first surface and the second surface into         contact; and     -   progressively releasing the strain.

Preferred but non-limiting features of the present invention are as follow:

-   -   the surface area of a convex hull formed by the set of pressure         points is null and the surface area of the convex hull formed by         the set of support and pressure points is non-null;     -   the first substrate is held by suckers or suction cups placed at         the support points,     -   each sucker or suction cup is linked to a telescopic arm;     -   the second substrate is placed on a support comprising at least         two spacers respectively on each sides of the second substrate,         the at least two spacers being higher than the thickness of the         second substrate;     -   the first substrate is held by resting on the spacers, the         support points being points of contact between the spacers and         the first substrate;     -   the support comprises at least one sucker or suction cup for         holding the second substrate;     -   the strain is applied by at least one piston rod;     -   the first substrate is a glass sheet, and wherein the second         substrate is a silicon tile;     -   the first substrate is sequentially bonded to a plurality of         second substrates by applying a strain to the first substrate         per second substrate;     -   the at least one piston rod is mounted on a mobile device and         sequentially applies each strain to the first substrate; and     -   the first substrate is simultaneously bonded to a plurality of         second substrates by deforming the whole first substrate.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other features and advantages of this invention will be apparent in the following detailed description of an illustrative embodiment thereof, which is to be read in connection with the accompanying drawings wherein:

FIG. 1 previously described represents steps of a known process for making SiOG structures;

FIG. 2 previously described is a traversal view of a detail of a defect due to the presence of a bubble in an SOI structure;

FIG. 3 represents a bonding propagation wave during a molecular bonding;

FIG. 4 represents an embodiment of a step of holding a substrate in a process according to the invention;

FIGS. 5 a-5 e represent an alternative embodiment of a step of holding a substrate in a process according to the invention;

FIGS. 6 a-6 d represent successive steps of an embodiment of a process according to the invention;

FIGS. 7 a-7 b are upper views of alternative possible dispositions of substrates on a support in an embodiment of a process according to the invention; and

FIGS. 8 a-8 f represent successive steps of another embodiment of a process according to the invention.

DETAILED DESCRIPTION OF A PREFERRED EMBODIMENT

Referring to the drawings, a method according to a preferred embodiment of the invention will now be described.

To avoid the trapping of bubbles, the best solution is to carefully control the propagation of the bonding wave, as represented by FIG. 3. Indeed, the bonding wavefront is the curve delimiting at a given time the area already bonded (i.e., already traveled by the bonding wave), and extending toward unbounded areas by molecular attraction. A bubble is trapped if two distinct points of this curve join, thereby surrounding an unbound area. As air cannot escape from such a surrounded unbound area, the bonding wavefront stops. So, at any moment, the bonding wavefront has to be continuous.

In the represented case, the bonding starts by a contact at the point P1. Then, the bonding wavefront radially extents: L(t1), L(t2) and L(t3) represent the position of the bonding wavefront at three instants t1<t2<t3. From the central bonding initiation, the bonding wavefront extends up to the edges of the second substrate 1 b, expelling the air without trapping it.

In this context, the invention proposes a method for bonding a first substrate 1 a having a first surface 2 a to a second substrate 1 b having a second surface 2 b, in which the propagation of the bonding wave is controlled. The first substrate 1 a is held by at least two support points S1 and S2, positioned near (e.g., 100 to 1000 microns) the second substrate 1 b so that first surface 2 a and second surface 2 b face each other. The first substrate 1 a is deformed in order to have a single contact between the two surfaces 2 a and 2 b. This deformation is obtained by applying between at least one pressure point P1 different from the two support points S1 and S2 a strain F toward the second substrate 1 b, and then bringing the deformed first surface 2 a and the second surface 2 b into contact. The deformation may be performed until the deformed first surface 2 a and the second surface 2 b get into contact, or alternatively, the first substrate 1 a may be deformed, and then its first surface 1 a brought into contact with the second surface 2 a by translation once the deformation is complete. From this contact, which is located at the pressure point P1, the bonding wave is initiated. The warpage of the first substrate 1 a is about a few hundreds of micrometers, which is very small compared to the lateral dimensions of typically used substrates, i.e., a few hundreds of millimeters. For instance, the force needed for obtaining a warpage of 200 microns in the middle of a 775 micron thick silicon substrate having a surface of 20 cm×20 cm and supported at its edges is about 1.3 N, and the force needed for obtaining a warpage of 200 microns in the middle of a 500 micron thick silicon substrate having a surface of 20 cm×20 cm and supported at its edges is about 0.2 N.

A first embodiment is represented in FIG. 4. In this advantageous embodiment, the first substrate 1 a is held at four support points S1, S2, S3 and S4 by a vacuum system, a sucker or suction cup 3 being placed at each support point. The first substrate 1 a is then positioned within a few tenths of millimeters above the second substrate 1 b.

FIGS. 5 a-5 e show alternative geometries for support and pressure points that enable initiating the propagation of the bonding wave at different locations. Only two support points are required. The invention is not limited to any one of these geometries, and one skilled in the art would know how to place support and pressure points according to the shape and the material of the first substrate 1 a.

The geometry of support and pressure points may, for example, respect two conditions:

(1) at least two support points S1 and S2 have to be unaligned with at least one pressure point P1. In other words, the convex hull formed by the set of support and pressure points (i.e., the smallest polygon containing at least every point of this set) has to have a non-null surface area. However, there are no physical support means that are totally punctual: for example, a sucker or suction cup 3 enlarges upon several cm². Thus, if the suckers or suction cups 3 are large enough, geometries as represented by FIGS. 5 d and 5 e do not contradict this first condition and can be used in embodiment of the method according to the invention, as one sucker or suction cup 3 acts as a plurality of sufficiently distant support points.

(2) if there are at least three pressure points, they shall not form a triangle. In other words, the convex hull formed by the set of pressure points has to have a null surface area. If a triangle is formed, when contact between surfaces 2 a and 2 b is made, the bonding wavefront links the edges of the triangle, and air may be trapped inside. To the contrary, if all the pressure points are forming a line, no zone where air may be trapped appears.

The first substrate 1 a is then bent by applying the strain F between the at least one pressure point P1 and the support points S1, S2, for example, thanks to the movement of a piston rod 5 in contact with the first substrate 1 a at the pressure point P1. Besides, the contact between the piston rod 5 and the first substrate 1 a may be linear and not punctual, according to the second condition explained above. In this case the strain F is applied between the support points (S1, S2) and a pressure line P. When the two surfaces 2 a and 2 b get in contact, the molecular bonding initiates.

The applied strain deforms the first substrate 1 a such that a central portion of the first substrate portion initially contacts the second substrate surface. When the strain F is applied in a linear manner the central portion of the first substrate 1 a contacts the second substrate 1 b in a line of contact.

After the initial contact is made, the strain F can be progressively released to propagate a bonding wave, which bonds the substrates 1 a, 1 b together. This final step of releasing the strain F facilitates bonding of the substrates while minimizing or avoiding the trapping of air bubbles between the substrates 1 a, 1 b. The release of the strain F to let the bonding wave propagate can be conducted in a number of ways.

A first considered possibility is to simply release the vacuum at one stroke and provoke a high-speed propagation of the bonding wave. It was found, however, that this propagation is faster at the edge of the substrate than elsewhere. Thus, lateral parts of the bonding wavefront might join, whereas the central part has not yet reached the edge of the substrate and this might cause the trapping of air bubbles.

To prevent this risk, the solution proposed by the invention is to progressively, and not suddenly, release the strain F applied between the support and pressure points (S1, S2, P1 . . . ), in order to control at any time the propagation of the bonding wave. To this end, suckers or suction cups 3 may be, for example, mounted on telescopic arms 4.

Advantageously, in a variant of the method according to the invention, the first substrate 1 a is bonded to a plurality of second substrates 1 b. Indeed, the first substrate 1 a is, for example, a glass sheet, while the second substrate 1 b is a silicon tile. Large sheets of glass can be easily manufactured, so that they can receive a plurality of silicon substrates, as the substrates have generally a width between 20 cm and 30 cm. However, the invention is not limited to the bonding of glass and silicon substrates.

FIGS. 6 a-6 d schematically represent a bonding sequence of a first substrate 1 a and a plurality of second substrates 1 b according to a second advantageous embodiment of the invention.

Initially (FIG. 6 a), the second substrates 1 b are pre-positioned on a support 10 and maintained by an optional vacuum system of suckers or suction cups 12. The first substrate 1 a is then positioned and laid on spacers 11 located on each side of the second substrates 1 b (i.e., between two rows). These spacers 11 have a height exceeding the thickness of the second substrates 1 b, preferably by at least 200 μm. In the case of silicon tiles having a thickness of e.g., 775 μm, the height of spacers 11 therefore reaches at least 975 μm. The spacers 11 are support lines for the first substrate 1 a (there may however be a succession of dots instead).

During a second step (FIG. 6 b), the piston rod 5 applies the strain F. As already explained, the piston rod 5 can get in a punctual contact at the center of each tile or get in a linear contact (FIGS. 7 a and 7 b). The strain applied by piston rods 5 will then bend the first substrate 1 a in between the linear spacers 11. The mechanical contact is then obtained for the one or several second substrate(s) 1 b positioned between the spacers 11 and the first substrate 1 a. The nine tiles shown on FIG. 7 a may, for example, be bonded all the nine simultaneously (using nine pistons, or using three linear contact rods, not shown), or, for example, row by row (using three pistons as shown in FIG. 7 a), or, for example, one by one (using one piston, not shown).

The sucker or suction cup 12 is then released, so the second substrate 1 b becomes only held by the pressure point P1 where molecular bonding is made. The piston rod 5 is thus progressively shortened, the second substrate 1 b rising up from the support 10 as the bonding wavefront extends (FIG. 6 c). With a deformation of the first substrate 1 a corresponding to a displacement of its edges with respect to the pressure point P1 of at least 200 μm (due to the height of each spacer 11), it is possible to control the bonding wave speed so that the bonding wave velocity ideally in each point of the bonding interface does not exceed the minimum bonding wave velocity that is observed in the center area of the bonding interface during an uncontrolled bonding, to prevent the formation of bubbles. The invention enables the bonding wave speed velocity to be reduced in the center, as well as in the periphery of the bonding interface.

The bonding ends when the piston rod 5 reaches again its start position. The bonding wave has propagated over the whole surface of the second substrate 1 b (FIG. 6 d)

The method can then be applied on the next second substrate 1 b or line of second substrates 1 b. Advantageously, the piston rod 5 is mounted on a mobile device 6. This mobile device 6 is, for example, a 3-axis robot. It can move from one first line of substrates 1 b to another and sequentially applies the strain F to them.

According to another advantageous embodiment of the invention, the whole first substrate 1 a is deformed, and it is bound simultaneously to the plurality of second substrates 1 b. In this case, as it can be seen in FIG. 8 a, the bonding sequence begins with a step of pre-positioning the substrates 1 a, 1 b. The first substrate 1 a is held under vacuum by suckers or suction cups 3 at the extremity of telescopic arms 4 above a plurality of second substrates 1 b, which lay on the support 10. Each second substrate 1 b may be held by at least one sucker or suction cup 12 embedded in the support 10. The center of the first surface 2 a of substrate 1 a is kept at least 100 μm above from surfaces 2 b of the second substrates 1 b.

For deforming this substrate 1 a, a central element, for example, a piston rod 5, is in contact with the substrate 1 a at the pressure point P1. Suckers or suction cups 3 and telescopic arms 4 are movable in rotation so that the substrate 1 a can take a free form, imposed only by the support points S1 and S2 of contact between the substrate (1 a) and the suckers or suction cups 3, and the pressure point P1 of contact with the head of the piston rod 5. By lengthening the piston rod 5, the strain F is applied and the pressure point P1 gets closer to the substrates 1 b, as represented by FIG. 8 b.

A contact force of less than 10 N (e.g., 2-10 N) is applied to begin the molecular bonding (FIG. 8 c). The bonding propagation wave is then initiated by gradual release of the bending imposed on the first substrate 1 a. For this, the telescopic arms 4 are lengthened (FIG. 8 d). The speed of this release is limited so that a uniform bonding wavefront propagates between the two substrates 1 a-1 b.

When the bonding wavefront reaches other second substrates 1 b, as represented by FIG. 8 e, advantageously, auxiliary piston rods 5′ embedded in the structure 10 initiate bonding waves on the other second substrates 1 b. The bonding sequence ends when the strains applied on the entire first substrate 1 a are released (FIG. 8 f).

In particular, it is important to distinguish between two cases depending on whether the number of rows of second substrates 1 b is odd or even. When this number is even (as shown in FIG. 8), the first contact is made on the edge of the two central rows. If this number is odd, the first contact is in the middle of the central row. The bonding mechanism is the same for the lateral rows.

This embodiment of the method according to the invention enables a high-speed industrial process, as a plurality of silicon tiles can be bound at once. Moreover, as only a small number of handlings are required, such a method guarantees a very precise bonding, leading to high-quality products.

Although the preceding description mentions suckers or suction cups, this is intended to include other vacuum members or devices that are able to provide suction for holding the substrates. 

What is claimed is:
 1. A method for bonding a first substrate having a first surface to a second substrate having a second surface, which comprises: holding the first substrate by at least two support points; positioning the first substrate and the second substrate so that the first surface and the second surface face each other; deforming the first substrate by applying between at least one pressure point and the at least two support points a strain toward the second substrate; bringing the deformed first surface and the second surface into contact; and progressively releasing the strain to facilitate bonding of the substrates while minimizing or avoiding the trapping of air bubbles between the substrates.
 2. The method according to claim 1, wherein the surface area of a convex hull formed by the set of pressure points is null and the surface area of a convex hull formed by the set of support and pressure points is non-null.
 3. The method according to claim 1, wherein the applied strain deforms the first substrate such that a central portion of the first substrate portion initially contacts the second substrate surface before the strain is released to propagate a bonding wave which bonds the substrates together.
 4. The method according to claim 3, wherein the strain is applied in a linear manner so that the central portion of the first substrate contacts the second substrate in a line of contact before the strain is released to propagate a bonding wave which bonds the substrates together.
 5. The method according to claim 1, wherein the first substrate is held by suckers or suction cups placed at the at least two support points.
 6. The method according to claim 5, wherein each sucker or suction cup is linked to a telescopic arm.
 7. The method according to claim 1, wherein the second substrate is placed on a support comprising at least two spacers located respectively on each side of the second substrate, with the spacers being thicker than the thickness of the second substrate.
 8. The method according to claim 7, wherein the first substrate is held by resting on the spacers, with the at least two support points being points of contact between the spacers and the first substrate.
 9. The method according to claim 7, wherein the support comprises at least one sucker or suction cup for holding the second substrate.
 10. The method according to claim 1, wherein the first substrate is a glass sheet, and wherein the second substrate is a silicon tile.
 11. The method according to claim 1, wherein the first substrate is sequentially bonded to a plurality of second substrates by sequentially applying strain.
 12. The method according to claim 1, wherein the first substrate is simultaneously bonded to a plurality of second substrates when the first substrate is deformed.
 13. A method for bonding a first substrate of a glass sheet having a first surface to a second substrate having a second surface, which comprises: holding the first substrate by at least two support points; positioning the first substrate and the second substrate so that the first surface and the second surface face each other; deforming the first substrate by applying between at least one pressure point and the at least two support points a strain toward the second substrate; bringing the deformed first surface and the second surface into contact; and progressively releasing the strain to facilitate bonding of the substrates while minimizing or avoiding the trapping of air bubbles between the substrates.
 14. The method according to claim 13, wherein the second substrate is a semiconductor substrate.
 15. The method according to claim 14, wherein the second substrate is a silicon substrate.
 16. The method according to claim 13, wherein the first substrate is simultaneously bonded to a plurality of second substrates when the first substrate is deformed. 